Ultrahigh vacuum scanning tunneling microscopy/magnickel oxide filmsnetic force microscopy study of ultrathin iron films grown on polycrystalline nickel oxide films

dc.contributor.authorDreyer, M.
dc.contributor.authorHwang, D. G.
dc.contributor.authorGomez, R. D.
dc.date.accessioned2008-08-06T17:51:08Z
dc.date.available2008-08-06T17:51:08Z
dc.date.issued2002-05-15
dc.description.abstractThe thickness dependence of the topographic and magnetic structure of ultrathin Fe films grown on polycrystalline NiO films under ultrahigh vacuum ~UHV! conditions was studied to investigate the growth mechanism of the ferromagnetic film and the corresponding magnetic interaction with the antiferromagnetic substrate. Externally prepared NiO films of 60 nm thickness were cleaned by heating in UHV. Ultrathin layers of Fe in the range of 1–27 nm were deposited on top of the NiO film and were analyzed at specific coverages. Iron grows as a polycrystalline film with the grains increasing in size with the thickness. The contours of the underlying NiO crystallites were evident at low coverages but gradually disappeared as the Fe grains coalesced at thicker coverages. Magnetic force microscopy images of the 1 nm thick film show randomly oriented magnetic grains with an average domain size of 30 nm. With an increase in film thickness the size of the domains grows to about 200 nm at 15 nm of iron. At a film thickness of 19 nm cross-tie domain walls become visible, indicating the crossover of some parts of the film from random magnetic grains into continuous domains with in-plane magnetization. A further increase in the film thickness leads to larger in-plane domains, while there are some areas with localized grains on the surface.en
dc.format.extent580945 bytes
dc.format.mimetypeapplication/pdf
dc.identifier.citationM. Dreyer, D. G. Hwang, and R. D. Gomez, "Ultrahigh vacuum scanning tunneling microscopy/magnetic force microscopy study of ultrathin iron films grown on polycrystalline nickel oxide films", J. Appl. Phys. 91, 8138 (2002)en
dc.identifier.urihttp://hdl.handle.net/1903/8298
dc.language.isoen_USen
dc.publisherAmerican Institute of Physicsen
dc.relation.isAvailableAtA. James Clark School of Engineeringen_us
dc.relation.isAvailableAtElectrical & Computer Engineeringen_us
dc.relation.isAvailableAtDigital Repository at the University of Marylanden_us
dc.relation.isAvailableAtUniversity of Maryland (College Park, MD)en_us
dc.rights.licenseCopyright 2002 American Institute of Physics. This article may be downloaded for personal use only. Any other use requires prior permission of the author and the American Institute of Physics. The following article may be found at http://jap.aip.org/.
dc.subjectferromagnetic filmen
dc.subjectantiferromagnetic substrateen
dc.titleUltrahigh vacuum scanning tunneling microscopy/magnickel oxide filmsnetic force microscopy study of ultrathin iron films grown on polycrystalline nickel oxide filmsen
dc.typeArticleen

Files

Original bundle
Now showing 1 - 1 of 1
Loading...
Thumbnail Image
Name:
Dreyer2002_2.pdf
Size:
567.33 KB
Format:
Adobe Portable Document Format
License bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
license.txt
Size:
1.8 KB
Format:
Item-specific license agreed upon to submission
Description: