New submissions to the thesis/dissertation collections are added automatically as they are received from the Graduate School. Currently, the Graduate School deposits all theses and dissertations from a given semester after the official graduation date. This means that there may be up to a 4 month delay in the appearance of a give thesis/dissertation in DRUM

More information is available at Theses and Dissertations at University of Maryland Libraries.

Browse

Filters

20131

Settings

Subject: search.filters.subject.metal hydride

Search Results

Now showing 1 - 1 of 1
  • Thumbnail Image
    Item
    Formation and Characterization of Transversely Modulated Nanostructures in Metallic Thin Films using Epitaxial Control
    (2013) Boyerinas, Brad Michael; Bruck, Hugh A; Mechanical Engineering; Digital Repository at the University of Maryland; University of Maryland (College Park, Md.)
    This thesis describes a fundamental investigation into the formation, characterization, and modeling of epitaxially-controlled self-assembly at the nanoscale. The presence of coherent nanophases and the clamping effect from an epitaxial substrate enables the formation of transversely modulated nanostructures (TMNS) resulting in improved functionality, which was previously observed through increased piezoelectric response in BiFeO3. The ability to fabricate high quality epitaxial films presents opportunity to investigate coherent phase decomposition in other material systems with multifunctional response. The research herein aims to extend the concept of nanoscale self assembly in metallic systems, including Ag-Si and Pd-PdH. First, the effect of annealing a Ag-Si couple was examined, and ordered, nanoscale Ag crystallites were observed along the interface with the epitaxial Si wafer. It is demonstrated that Ag foil can be used in place of doped Ag paste (commonly used in solar cell metallization) to achieve TMNS at the interface. It was proved that annealing the Ag-Si couple in air is necessary for the self-assembly reaction to take place, as doing so prevents bulk diffusion and eutectic melting. Electron backscatter diffraction was used to verify the epitaxial relation between the Ag nanostructures and Si crystal. A method to fabricate ordered, nanoscale PdH precipitates in epitaxial Pd thin films via high temperate gas phase hydrogenation was established. Epitaxial Pd films were deposited via e-beam deposition and a V buffer layer was necessary to induce epitaxy. This novel self-assembled nanostructure may enable hysteresis-less absorption and desorption, thus improving functionality with regard to hydrogen sensing and storage. The epitaxial Pd film was characterized before and after hydrogenation with x-ray diffraction and atomic force microscopy to determine composition and nanostructure of the film. A thermodynamic model was developed to demonstrate the possibility to control or eliminate thermodynamic hysteresis via balance of elastic interaction between the coherent interfaces of metal and metal-hydride phases and the film-substrate interface. This model can be extended to other metal-hydride systems which demonstrate coherent phase decomposition.