Arcing Failure of ROHS Compliant Electromagnetic Relays

Simple item page
dc.contributor.advisorMcCluskey, F. Patricken_US
dc.contributor.authorBoettcher, Robert Donalden_US
dc.contributor.departmentMechanical Engineeringen_US
dc.contributor.publisherDigital Repository at the University of Marylanden_US
dc.contributor.publisherUniversity of Maryland (College Park, Md.)en_US
dc.date.accessioned2013-02-07T07:24:26Z
dc.date.available2013-02-07T07:24:26Z
dc.date.issued2012en_US
dc.description.abstractElectronic relay contacts have traditionally been made of materials, primarily Ag/CdO, which are resistant to welding under short, high power pulses. However, since 2006, RoHS prohibits the use of cadmium in electronics, driving the elimination of Ag/CdO and its replacement with Ag/SnO2. The reliability of relays made with Ag/SnO2 contacts has been shown to be vendor specific. This thesis focuses on developing an understanding of the metallurgical and design factors that vary by manufacturer and their effect on welding susceptibility of Ag/SnO2 electromagnetic relay contacts and other related relay failure mechanisms. In addition, it aims to predict a safe operating area of power and energy over which specific relay contacts will not weld under high power DC conditions. Relays from various manufacturers were subjected to capacitor discharge pulses of 250 V at 10-80 uF to characterize relay reliability. Failure analysis was then conducted on the welded contacts using scanning electron microscopy (SEM) and wavelength-dispersive spectroscopy (WDS) in order to address material properties and design variations that affect the welding susceptibility of relays. The incidence and extent of degradation is correlated to material characteristics including contact composition, oxide content, hardness, contact geometry, and surface roughness using a physics of failure approach. The relays with a higher percent content of indium oxide exhibited a greater reliability than those without. Both power and energy were then varied to further investigate the one cycle to failure boundary region and a failure map is presented.en_US
dc.identifier.urihttp://hdl.handle.net/1903/13658
dc.subject.pqcontrolledMechanical engineeringen_US
dc.subject.pqcontrolledElectrical engineeringen_US
dc.subject.pquncontrolledArc Failureen_US
dc.subject.pquncontrolledContactsen_US
dc.subject.pquncontrolledRelaysen_US
dc.subject.pquncontrolledWeldingen_US
dc.titleArcing Failure of ROHS Compliant Electromagnetic Relaysen_US
dc.typeThesisen_US

Files

Original bundle
Now showing 1 - 1 of 1
Thumbnail Image
Name:
Boettcher_umd_0117N_13907.pdf
Size:
3.98 MB
Format:
Adobe Portable Document Format
Download

Collections

UMD Theses and Dissertations
Mechanical Engineering Theses and Dissertations